國立虎尾科技大學 |

Development of Alkali Barium Glasses for Hermetic Applications = Sızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi /

Record Type:	Language materials, printed : Monograph/item
Title/Author:	Development of Alkali Barium Glasses for Hermetic Applications/ Tutku Turgutlugil Gökçe.
Reminder of title:	Sızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi /
Author:	Gökçe, Tutku Turgutlugil,
Description:	1 electronic resource (125 pages)
Notes:	Source: Masters Abstracts International, Volume: 86-04.
Contained By:	Masters Abstracts International86-04.
Subject:	Barium. -
Online resource:	http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=31656171
ISBN:	9798342370639

Development of Alkali Barium Glasses for Hermetic Applications = Sızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi /
Gökçe, Tutku Turgutlugil,

Development of Alkali Barium Glasses for Hermetic ApplicationsSızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi / [electronic resource] =Tutku Turgutlugil Gökçe. - 1 electronic resource (125 pages)

Source: Masters Abstracts International, Volume: 86-04.

Alkali barium glasses in the SiO2, Al2O3, LiO2, K2O, Na2O, and BaO system were prepared using high-purity powders by the melt-quench technique to evaluate the compatibility of these glasses for hermetic sealing. The melting process took place at the laboratory conditions at 1550 °C for 30 min. Six different glasses with varying Na2O and K2O content were produced. The total Na2O + K2O content in the glasses was kept constant at 15 wt% but, the Na2O/K2O ratio was adjusted. Glasses were cast into a molybdenum mold to get rectangular prism shaped samples for the density, coefficient of thermal expansion (CTE), and chemical durability measurements. Results indicated that even a slight change in Na2O/K2O led to notable changes in the glass properties. Glass pellets were subsequently sealed with 304 stainless steel using different sealing profiles under argon gas. The results revealed that the sealing and crystallization temperature of the sealing profile, and the composition of the glass have a profound effect in the microstructure of the compression sealing developed between the alkali barium glass and 304 stainless steels.

English

ISBN: 9798342370639Subjects--Topical Terms:

1467528
Barium.

Development of Alkali Barium Glasses for Hermetic Applications = Sızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi /
LDR:03789nam a22004093i 4500 001 1172892
005 20260622113221.5
006 m o d
007 cr|nu||||||||
008 260803s2024 miu||||||m |||||||eng d
020 $a 9798342370639
035 $a (MiAaPQD)AAI31656171
035 $a (MiAaPQD)MiddleEastTech108479
035 $a AAI31656171
040 $a MiAaPQD $b eng $c MiAaPQD $e rda
100 1 $a Gökçe, Tutku Turgutlugil, $e author. $3 1503518
245 1 0 $a Development of Alkali Barium Glasses for Hermetic Applications $b Sızdırmazlık Uygulamaları Için Alkali Baryum Camlarının Geliştirilmesi / $c Tutku Turgutlugil Gökçe. $h [electronic resource] =
264 1 $a Ann Arbor : $b ProQuest Dissertations & Theses, $c 2024
300 $a 1 electronic resource (125 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Masters Abstracts International, Volume: 86-04.
500 $a Advisors: Öztürk, Abdullah.
502 $b M.S. $c Middle East Technical University (Turkey) $d 2024.
520 # $a Alkali barium glasses in the SiO2, Al2O3, LiO2, K2O, Na2O, and BaO system were prepared using high-purity powders by the melt-quench technique to evaluate the compatibility of these glasses for hermetic sealing. The melting process took place at the laboratory conditions at 1550 °C for 30 min. Six different glasses with varying Na2O and K2O content were produced. The total Na2O + K2O content in the glasses was kept constant at 15 wt% but, the Na2O/K2O ratio was adjusted. Glasses were cast into a molybdenum mold to get rectangular prism shaped samples for the density, coefficient of thermal expansion (CTE), and chemical durability measurements. Results indicated that even a slight change in Na2O/K2O led to notable changes in the glass properties. Glass pellets were subsequently sealed with 304 stainless steel using different sealing profiles under argon gas. The results revealed that the sealing and crystallization temperature of the sealing profile, and the composition of the glass have a profound effect in the microstructure of the compression sealing developed between the alkali barium glass and 304 stainless steels.
520 3 $a Bu çalışmada; SiO2, Al2O3, LiO2, K2O, Na2O ve BaO sistemindeki alkali baryum camları, yüksek saflıkta tozlar kullanılarak eritme-soğutma tekniği ile hazırlandı. Bu camların hermetik mühürleme için uygunluğunu değerlendirmek amacıyla eritme işlemi laboratuvar koşullarında 1550 °C'de 30 dakika boyunca gerçekleştirildi. Değişen Na2O ve K2O içeriğine sahip altı farklı cam üretildi. Camlardaki toplam Na2O + K2O içeriği 15% sabit tutuldu ancak Na2O/K2O oranı ayarlandı. Camlar, yoğunluk, termal genleşme katsayısı (CTE) ve kimyasal dayanıklılık ölçümleri için dikdörtgen prizma şeklinde numuneler elde etmek için molibden kalıba döküldü. Sonuçlar, Na2O/K2O'da küçük bir değişikliğin bile cam özelliklerinde dikkate değer değişikliklere yol açtığını gösterdi. Cam pelletleri daha sonra argon gazı altında farklı mühürleme profilleri kullanılarak 304 paslanmaz çelik ile mühürlendi. Sonuçlar, mühürleme profili, mühürleme ve kristallenme sıcaklığı ile camın kompozisyonunun, alkali baryum camı ile 304 paslanmaz çelik arasında geliştirilen sıkıştırma mühürünün mikroyapısı üzerinde derin bir etkisi olduğunu ortaya koydu.
546 $a English
590 $a School code: 2013
650 # 4 $a Barium. $3 1467528
650 # 4 $a Metals. $3 563369
650 # 4 $a Cooling. $3 812392
650 # 4 $a Spectrum analysis. $3 582358
650 # 4 $a Stainless steel. $3 716611
650 # 4 $a Metal oxides. $3 1437682
650 # 4 $a Chemical bonds. $3 654810
650 # 4 $a Packaging. $3 999828
650 # 4 $a Potash. $3 1372562
650 # 4 $a Contact angle. $3 1049700
650 # 4 $a Scanning electron microscopy. $3 768680
650 # 4 $a Corrosion. $3 995076
650 # 4 $a Analytical chemistry. $3 1182118
650 # 4 $a Materials science. $3 557839
650 # 4 $a Optics. $3 595336
690 $a 0549
690 $a 0486
690 $a 0794
690 $a 0752
710 2 # $a Middle East Technical University (Turkey). $b Department of Metallurgical and Materials Engineering. $e degree granting institution. $3 1503519
720 1 $a Öztürk, Abdullah $e degree supervisor.
773 0 # $t Masters Abstracts International $g 86-04.
790 $a 2013
791 $a M.S.
792 $a 2024
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=31656171