Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.

Record Type:	Language materials, manuscript : Monograph/item
Title/Author:	Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells./
Author:	Panchal, Tarang Kiran.
Description:	1 online resource (72 pages)
Notes:	Source: Masters Abstracts International, Volume: 85-01.
Contained By:	Masters Abstracts International85-01.
Subject:	Cadmium telluride. -
Online resource:	click for full text (PQDT)
ISBN:	9798379882129

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
Panchal, Tarang Kiran.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells. - 1 online resource (72 pages)

Source: Masters Abstracts International, Volume: 85-01.

Thesis (M.Sc.)--Purdue University, 2023.

Includes bibliographical references

The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young's Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.

Electronic reproduction.
Ann Arbor, Mich. :
ProQuest,
2024

Mode of access: World Wide Web

ISBN: 9798379882129Subjects--Topical Terms:

1466221
Cadmium telluride.
Index Terms--Genre/Form:

554714
Electronic books.

Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
LDR:02809ntm a22004097 4500 001 1142063
005 20240414211935.5
006 m o d
007 cr mn ---uuuuu
008 250605s2023 xx obm 000 0 eng d
020 $a 9798379882129
035 $a (MiAaPQ)AAI30540038
035 $a (MiAaPQ)Purdue22783613
035 $a AAI30540038
040 $a MiAaPQ $b eng $c MiAaPQ $d NTU
100 1 $a Panchal, Tarang Kiran. $3 1466220
245 1 0 $a Effect of Temperature on the Delamination and Performance of Monocrystalline Silicon Solar Cells.
264 0 $c 2023
300 $a 1 online resource (72 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Masters Abstracts International, Volume: 85-01.
500 $a Advisor: Kim, Hansung.
502 $a Thesis (M.Sc.)--Purdue University, 2023.
504 $a Includes bibliographical references
520 $a The solar cells degrade over time in the field due to various environmental conditions including temperature and humidity. Accelerated lifetime testing was used to test solar cells in a short period of time to obtain reliability and predict the lifetime. Accelerated lifetime testing was done on two 10-WATT ACOPOWER rigid mono crystalline silicon solar panel, 2 3-WATT semi-flexible monocrystalline silicon solar panel and 30 Sunyima Mini Monocrystalline Solar Cell to calculate the acceleration factor, mean reliable life through statistical analysis at certain working conditions. Two Damp heat tests were conducted on the samples to find the degradation and potential defects that occur in the solar cell and that data was used for the statistical analysis. Reliasoft ALTA software was used to statistically analyze the experimental data and to predict the lifetime and to find the probability of failure of the solar cells.Peeling tests were conducted to find the adhesion strength between layers of the untested solar cell samples and accelerated life testing (ALT) tested solar cell samples. Tensile tests were conducted to find out the Young's Modulus, yield stress and yield strain of the peel arm from the peeling test. The data from the tests were used to calculate the energy release rate or the fracture energy. A multivariable Regression analysis was done to develop an analytical equation between the energy release rate (Gc) and Temperature & Humidity.
533 $a Electronic reproduction. $b Ann Arbor, Mich. : $c ProQuest, $d 2024
538 $a Mode of access: World Wide Web
650 4 $a Cadmium telluride. $3 1466221
650 4 $a Thermal cycling. $3 1466217
650 4 $a Humidity. $3 1168172
650 4 $a Failure. $3 1365603
650 4 $a Solar energy. $3 565705
650 4 $a Electricity. $3 599451
650 4 $a Weather. $3 994153
650 4 $a Yield stress. $3 1466222
650 4 $a Electric rates. $3 1466223
650 4 $a Adhesion. $3 712668
650 4 $a Photovoltaic cells. $3 564666
650 4 $a Silicon wafers. $3 1372662
650 4 $a Heat. $3 1276837
650 4 $a Adhesives. $3 559224
650 4 $a Ultraviolet radiation. $3 768819
650 4 $a Corrosion. $3 995076
650 4 $a Alternative energy. $3 1241221
650 4 $a Atmospheric sciences. $3 1179392
650 4 $a Condensed matter physics. $3 1148471
650 4 $a Energy. $3 784773
650 4 $a Industrial engineering. $3 679492
650 4 $a Meteorology. $3 554820
650 4 $a Physics. $3 564049
655 7 $a Electronic books. $2 local $3 554714
690 $a 0363
690 $a 0725
690 $a 0611
690 $a 0791
690 $a 0546
690 $a 0629
690 $a 0557
690 $a 0605
710 2 $a ProQuest Information and Learning Co. $3 1178819
710 2 $a Purdue University. $3 1184550
773 0 $t Masters Abstracts International $g 85-01.
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30540038 $z click for full text (PQDT)