Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors.

Record Type:	Language materials, manuscript : Monograph/item
Title/Author:	Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors./
Author:	Jogineedi, Rohit.
Description:	1 online resource (128 pages)
Notes:	Source: Dissertations Abstracts International, Volume: 83-09, Section: B.
Contained By:	Dissertations Abstracts International83-09B.
Subject:	Mechanical engineering. -
Online resource:	click for full text (PQDT)
ISBN:	9798209882824

Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors.
Jogineedi, Rohit.

Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors. - 1 online resource (128 pages)

Source: Dissertations Abstracts International, Volume: 83-09, Section: B.

Thesis (Ph.D.)--Southern Illinois University at Carbondale, 2021.

Includes bibliographical references

Friction interaction between brake materials see a rise in temperatures of over 1000 oC contributing to thermal fade of brakes and deterioration/cracking of rotors. Various microstructural features like graphite, ferrite and pearlite could influence the mechanical and thermal properties and related friction performance of the brake materials. Even more relevant impact on properties and friction performance of rotors can be expected after coatings or surface treatments. The primary purpose of this research is to identify the impact of microstructure and surface treatment on properties and friction performance of four types of pearlitic gray cast irons. The C30, C20 and FC150 rotors were surface treated by bombarding with heavy ions which diffused into cast iron and created a coating with different chemistry and properties when compared to the "non-treated" rotors. Complete chemical and material characterization of the brake rotors using optical emission spectrometer (OES), carbon-sulfur combustion analyzer, polarized light microscopy, density (analytical balance and Archimedes principle), Brinell hardness tester, laser flash apparatus, scanning electron microscopy, and energy dispersive X-ray microanalysis. The pearlitic gray cast iron rotors are typified by the presence of graphite, carbides, and inclusions in an almost fully pearlitic matrix with a minimum amount (2-4 vol.%) of "free" ferrite. Graphite can be further classified based on its morphology. The investigated cast irons contained two different graphite types: type VII-E5 for the F150 OEM rotor, and type VII-C5 characteristic for the ASTM A48 classes C30 and C20, as well as the "Japanese" JIS G5501 FC150 rotors. It was identified from the initial curve fitting models that the observed microstructural differences in individual cast iron types are responsible for the observed mechanical (density - decreases with increasing ferrite and decreasing pearlite contents; hardness - decreases with increasing ferrite contents) and thermal properties (increase with increasing ferrite and pearlite contents), and friction performance (increases with increasing ferrite and decreasing graphite contents) of the studied rotors. The applied surface treatment also contributed to the modification of the mechanical and thermal properties, as well as friction performance of the studied rotors. However, there were not enough statistically relevant models developed from the generated data, which could identify the combined influence of various microstructural features observed and applied surface treatment over the properties and friction performance of the studied rotors.

Electronic reproduction.
Ann Arbor, Mich. :
ProQuest,
2024

Mode of access: World Wide Web

ISBN: 9798209882824Subjects--Topical Terms:

557493
Mechanical engineering.
Subjects--Index Terms:

FrictionIndex Terms--Genre/Form:

554714
Electronic books.

Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors.
LDR:04044ntm a22003857 4500 001 1145447
005 20240624103653.5
006 m o d
007 cr bn ---uuuuu
008 250605s2021 xx obm 000 0 eng d
020 $a 9798209882824
035 $a (MiAaPQ)AAI28775910
035 $a AAI28775910
040 $a MiAaPQ $b eng $c MiAaPQ $d NTU
100 1 $a Jogineedi, Rohit. $3 1437678
245 1 0 $a Impact of Cast Iron Microstructure and Surface Treatment on Properties and Friction Performance of Brake Rotors.
264 0 $c 2021
300 $a 1 online resource (128 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Dissertations Abstracts International, Volume: 83-09, Section: B.
500 $a Advisor: Filip, Peter.
502 $a Thesis (Ph.D.)--Southern Illinois University at Carbondale, 2021.
504 $a Includes bibliographical references
520 $a Friction interaction between brake materials see a rise in temperatures of over 1000 oC contributing to thermal fade of brakes and deterioration/cracking of rotors. Various microstructural features like graphite, ferrite and pearlite could influence the mechanical and thermal properties and related friction performance of the brake materials. Even more relevant impact on properties and friction performance of rotors can be expected after coatings or surface treatments. The primary purpose of this research is to identify the impact of microstructure and surface treatment on properties and friction performance of four types of pearlitic gray cast irons. The C30, C20 and FC150 rotors were surface treated by bombarding with heavy ions which diffused into cast iron and created a coating with different chemistry and properties when compared to the "non-treated" rotors. Complete chemical and material characterization of the brake rotors using optical emission spectrometer (OES), carbon-sulfur combustion analyzer, polarized light microscopy, density (analytical balance and Archimedes principle), Brinell hardness tester, laser flash apparatus, scanning electron microscopy, and energy dispersive X-ray microanalysis. The pearlitic gray cast iron rotors are typified by the presence of graphite, carbides, and inclusions in an almost fully pearlitic matrix with a minimum amount (2-4 vol.%) of "free" ferrite. Graphite can be further classified based on its morphology. The investigated cast irons contained two different graphite types: type VII-E5 for the F150 OEM rotor, and type VII-C5 characteristic for the ASTM A48 classes C30 and C20, as well as the "Japanese" JIS G5501 FC150 rotors. It was identified from the initial curve fitting models that the observed microstructural differences in individual cast iron types are responsible for the observed mechanical (density - decreases with increasing ferrite and decreasing pearlite contents; hardness - decreases with increasing ferrite contents) and thermal properties (increase with increasing ferrite and pearlite contents), and friction performance (increases with increasing ferrite and decreasing graphite contents) of the studied rotors. The applied surface treatment also contributed to the modification of the mechanical and thermal properties, as well as friction performance of the studied rotors. However, there were not enough statistically relevant models developed from the generated data, which could identify the combined influence of various microstructural features observed and applied surface treatment over the properties and friction performance of the studied rotors.
533 $a Electronic reproduction. $b Ann Arbor, Mich. : $c ProQuest, $d 2024
538 $a Mode of access: World Wide Web
650 4 $a Mechanical engineering. $3 557493
650 4 $a Materials science. $3 557839
653 $a Friction
653 $a Graphite
653 $a Gray cast iron
653 $a Microstructure
653 $a Thermal properties
655 7 $a Electronic books. $2 local $3 554714
690 $a 0548
690 $a 0794
710 2 $a ProQuest Information and Learning Co. $3 1178819
710 2 $a Southern Illinois University at Carbondale. $b Engineering Science. $3 1180310
773 0 $t Dissertations Abstracts International $g 83-09B.
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=28775910 $z click for full text (PQDT)