Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys.

紀錄類型:	書目-語言資料,手稿 : Monograph/item
正題名/作者:	Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys./
作者:	Liu, Sufeng.
面頁冊數:	1 online resource (160 pages)
附註:	Source: Masters Abstracts International, Volume: 84-07.
Contained By:	Masters Abstracts International84-07.
標題:	Engineering. -
電子資源:	click for full text (PQDT)
ISBN:	9798368434001

Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys.
Liu, Sufeng.

Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys. - 1 online resource (160 pages)

Source: Masters Abstracts International, Volume: 84-07.

Thesis (M.A.Sc.)--University of Windsor (Canada), 2023.

Includes bibliographical references

A eutectic Al Alloy containing 1.8 wt.% Fe was cast by using a permanent steel mold casting (PMSC) with three different section thicknesses of 2, 8, 20 mm, and also squeeze cast (SC) with a cross-sectional thickness of 20 mm under an applied pressure of90 MPa. First, the difference in mechanical and electrical properties between the PSMC eutectic Al-1.8Fe Alloy and commercial-purity (CP) Al (99.7%) was investigated. The results showed that the ultimate tensile strength (UTS), yield strength (YS) of the cast CPAl significantly increased to 86.5 and 28.3 MPa from 34.5 and 12.3 MPa. However, the elongation (ef) and electrical conductivity (σ) of the cast alloy decreased to 19.8% and48.4 %IACS from 33.8% and 58.5 %IACS. The large area fraction (9.5%) of the micron and nano eutectic Al-Fe phases in the PSMC Al-1.8%Fe alloy should be responsible for the difference in mechanical and electrical properties between the PSMC Al-1.8%Fealloy and the PSMC CP Al. Secondly, the effect of section thicknesses on microstructure, mechanical and electrical properties of the PSMC Al-1.8Fe alloy was studied. The UTS,YS, ef, and elastic modulus (E) of the alloy increased, when the section thickness of the PSMC Al-1.8Fe decreased to 2 mm from 20 mm. However, the porosity level increased to 1.87% from 5.17% with increasing the thickness to 20 mm from 2 mm, respectively. The fine microstructure and low porosity level resulted in the high properties of the 2 mm sample. The study on the SC alloy indicated that the casting process increased the properties. The strain-hardening rate of the SC Al-1.8Fe alloy during plastic deformation was higher than that of the PSMC specimen. The high mechanical properties and electrical conductivities of the SC sample should be attributed to its fine microstructure and low porosity level compared to that of the PSMC counterpart.

Electronic reproduction.
Ann Arbor, Mich. :
ProQuest,
2024

Mode of access: World Wide Web

ISBN: 9798368434001Subjects--Topical Terms:

561152
Engineering.
Subjects--Index Terms:

Eutectic Al alloyIndex Terms--Genre/Form:

554714
Electronic books.

Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys.
LDR:03078ntm a22003377 4500 001 1145462
005 20240624103658.5
006 m o d
007 cr bn ---uuuuu
008 250605s2023 xx obm 000 0 eng d
020 $a 9798368434001
035 $a (MiAaPQ)AAI30244029
035 $a AAI30244029
040 $a MiAaPQ $b eng $c MiAaPQ $d NTU
100 1 $a Liu, Sufeng. $3 1437704
245 1 0 $a Mechanical and Electrical Properties and Microstructure of PSMC and SC Al-1.8Fe Alloys.
264 0 $c 2023
300 $a 1 online resource (160 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Masters Abstracts International, Volume: 84-07.
500 $a Advisor: Hu, Henry.
502 $a Thesis (M.A.Sc.)--University of Windsor (Canada), 2023.
504 $a Includes bibliographical references
520 $a A eutectic Al Alloy containing 1.8 wt.% Fe was cast by using a permanent steel mold casting (PMSC) with three different section thicknesses of 2, 8, 20 mm, and also squeeze cast (SC) with a cross-sectional thickness of 20 mm under an applied pressure of90 MPa. First, the difference in mechanical and electrical properties between the PSMC eutectic Al-1.8Fe Alloy and commercial-purity (CP) Al (99.7%) was investigated. The results showed that the ultimate tensile strength (UTS), yield strength (YS) of the cast CPAl significantly increased to 86.5 and 28.3 MPa from 34.5 and 12.3 MPa. However, the elongation (ef) and electrical conductivity (σ) of the cast alloy decreased to 19.8% and48.4 %IACS from 33.8% and 58.5 %IACS. The large area fraction (9.5%) of the micron and nano eutectic Al-Fe phases in the PSMC Al-1.8%Fe alloy should be responsible for the difference in mechanical and electrical properties between the PSMC Al-1.8%Fealloy and the PSMC CP Al. Secondly, the effect of section thicknesses on microstructure, mechanical and electrical properties of the PSMC Al-1.8Fe alloy was studied. The UTS,YS, ef, and elastic modulus (E) of the alloy increased, when the section thickness of the PSMC Al-1.8Fe decreased to 2 mm from 20 mm. However, the porosity level increased to 1.87% from 5.17% with increasing the thickness to 20 mm from 2 mm, respectively. The fine microstructure and low porosity level resulted in the high properties of the 2 mm sample. The study on the SC alloy indicated that the casting process increased the properties. The strain-hardening rate of the SC Al-1.8Fe alloy during plastic deformation was higher than that of the PSMC specimen. The high mechanical properties and electrical conductivities of the SC sample should be attributed to its fine microstructure and low porosity level compared to that of the PSMC counterpart.
533 $a Electronic reproduction. $b Ann Arbor, Mich. : $c ProQuest, $d 2024
538 $a Mode of access: World Wide Web
650 4 $a Engineering. $3 561152
650 4 $a Materials science. $3 557839
653 $a Eutectic Al alloy
655 7 $a Electronic books. $2 local $3 554714
690 $a 0794
690 $a 0537
710 2 $a ProQuest Information and Learning Co. $3 1178819
710 2 $a University of Windsor (Canada). $b ENGINEERING MATERIALS. $3 845537
773 0 $t Masters Abstracts International $g 84-07.
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=30244029 $z click for full text (PQDT)