Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates.

Record Type:	Language materials, manuscript : Monograph/item
Title/Author:	Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates./
Author:	Jenket, Donald Robert, II.
Description:	1 online resource (240 pages)
Notes:	Source: Dissertation Abstracts International, Volume: 78-12(E), Section: B.
Contained By:	Dissertation Abstracts International78-12B(E).
Subject:	Materials science. -
Online resource:	click for full text (PQDT)
ISBN:	9780355062625

Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates.
Jenket, Donald Robert, II.

Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates. - 1 online resource (240 pages)

Source: Dissertation Abstracts International, Volume: 78-12(E), Section: B.

Thesis (Ph.D.)

Includes bibliographical references

This item is not available from ProQuest Dissertations & Theses.

The effects of temperature and strain-rate on the mechanical properties of Ultra High Molar Mass Polyethylene (UHMMPE) single fibers was investigated at eleven temperatures from room temperature (20 °C) to the orthorhombic-hexagonal phase transition (148 °C) and at six strain-rates from quasi-static (10 -3 s-1) to dynamic (103 s-1). Dimensional analysis of ballistic limit tests using has shown an underperformance of materials comprised of UHMMPE fibers. A possible explanation is the relatively low melting temperature of UHMMPE fibers (&sim;150 °C) in comparison to other fiber materials, such as poly-aramids (&sim;450 °C).

Electronic reproduction.
Ann Arbor, Mich. :
ProQuest,
2018

Mode of access: World Wide Web

ISBN: 9780355062625Subjects--Topical Terms:

557839
Materials science.
Index Terms--Genre/Form:

554714
Electronic books.

Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates.
LDR:03786ntm a2200373Ki 4500 001 911204
005 20180529081859.5
006 m o u
007 cr mn||||a|a||
008 190606s2017 xx obm 000 0 eng d
020 $a 9780355062625
035 $a (MiAaPQ)AAI10270569
035 $a (MiAaPQ)umd:17991
035 $a AAI10270569
040 $a MiAaPQ $b eng $c MiAaPQ
099 $a TUL $f hyy $c available through World Wide Web
100 1 $a Jenket, Donald Robert, II. $3 1182890
245 1 0 $a Failure Mechanisms of Ultra High Molar Mass Polyethylene Single Fibers at Extreme Temperatures and Strain-Rates.
264 0 $c 2017
300 $a 1 online resource (240 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Dissertation Abstracts International, Volume: 78-12(E), Section: B.
500 $a Adviser: Mohamad Al-Sheikhly.
502 $a Thesis (Ph.D.) $c University of Maryland, College Park $d 2017.
504 $a Includes bibliographical references
506 $a This item is not available from ProQuest Dissertations & Theses.
520 $a The effects of temperature and strain-rate on the mechanical properties of Ultra High Molar Mass Polyethylene (UHMMPE) single fibers was investigated at eleven temperatures from room temperature (20 °C) to the orthorhombic-hexagonal phase transition (148 °C) and at six strain-rates from quasi-static (10 -3 s-1) to dynamic (103 s-1). Dimensional analysis of ballistic limit tests using has shown an underperformance of materials comprised of UHMMPE fibers. A possible explanation is the relatively low melting temperature of UHMMPE fibers (&sim;150 °C) in comparison to other fiber materials, such as poly-aramids (&sim;450 °C).
520 $a The mechanical properties of UHMMPE single fibers were investigated through a series of 437 tensile tests at 66 temperature-strain-rate combinations. Changes in stress-strain curve shapes were observed with respect to temperature and strain-rate. The transition of stress-curve shape with increasing temperature was observed to be pseudo-brittle, plateauing, necking, and non-failure and transitions between these phases were observed within a strain-rate dependent temperature range. For low and intermediate strain rates, a temperature and strain-rate equivalence is observed: a decadal increase of strain-rate is mechanically equivalent to a &sim;20 °C decrease in temperature. Strain to failure for dynamic strain rates was invariant over the temperature range of this study. Strength and modulus properties were observed to decrease with increasing temperature and increase with increasing strain-rate. An orthorhombic to hexagonal phase transition occurs between 145 °C and 148 °C and a sudden decrease in strength and moduli was observed.
520 $a The change in dominant stress-relieving mechanism is proposed. Chain slippage is dominant for the majority of conditions in this study except where scission and straightening are the dominant mechanism. At high temperatures for constrained fibers in the hexagonal phase, chain slippage occurs more frequently due to the trans to gauche conformation. Chain scission is only dominant moments before fiber failure and near the failure surface. Chain straightening is dominant at low strain (0 % to 0.5 %) and at temperatures greater than or equal to the necking temperatures for the quasi-static and intermediate strain-rates and at all temperatures for the dynamic strain-rates.
533 $a Electronic reproduction. $b Ann Arbor, Mich. : $c ProQuest, $d 2018
538 $a Mode of access: World Wide Web
650 4 $a Materials science. $3 557839
655 7 $a Electronic books. $2 local $3 554714
690 $a 0794
710 2 $a ProQuest Information and Learning Co. $3 1178819
710 2 $a University of Maryland, College Park. $b Material Science and Engineering. $3 1182891
773 0 $t Dissertation Abstracts International $g 78-12B(E).
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10270569 $z click for full text (PQDT)