Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments.

紀錄類型:	書目-語言資料,手稿 : Monograph/item
正題名/作者:	Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments./
作者:	Howard, Brent Ernest.
面頁冊數:	1 online resource (148 pages)
附註:	Source: Masters Abstracts International, Volume: 56-06.
標題:	Mechanical engineering. -
電子資源:	click for full text (PQDT)
ISBN:	9780355265408

Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments.
Howard, Brent Ernest.

Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments. - 1 online resource (148 pages)

Source: Masters Abstracts International, Volume: 56-06.

Thesis (M.S.)--University of Hawai'i at Manoa, 2017.

Includes bibliographical references

The environmental corrosion of carbon-fiber/epoxy and E-glass/epoxy composite laminated aluminum alloys [e.g., Al 1100-H14, Al 5456-H116 (non-sensitized), Al 5456-H116 (sensitized), and Al 7075-T6] was studied to characterize the interfacial corrosion between the composite and the aluminum substrate. Samples were exposed at 5 locations around the islands of Hawai'i that represented alpine, marine, severe marine, rainforest, and volcano environments over 1-month, 6- month, and 12-month time periods. After exposure, the samples were then adhesion strength tested by conducting pull test to remove the composite laminate from the aluminum substrate to determine the loss (if any) of the composite laminate adhesion to their respective aluminum substrates. The delaminated samples were then analyzed with a scanning electron microscope and energy dispersive X-ray analysis to determine the distribution of corrosion products and ionic species at the aluminum substrate - composite laminate interfaces. The decay in adhesion strength was correlated to the amount of corrosion at the interface that was dependent on the type of composite and type of aluminum alloy.

Electronic reproduction.
Ann Arbor, Mich. :
ProQuest,
2018

Mode of access: World Wide Web

ISBN: 9780355265408Subjects--Topical Terms:

557493
Mechanical engineering.
Index Terms--Genre/Form:

554714
Electronic books.

Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments.
LDR:02331ntm a2200325K 4500 001 913379
005 20180618102643.5
006 m o u
007 cr mn||||a|a||
008 190606s2017 xx obm 000 0 eng d
020 $a 9780355265408
035 $a (MiAaPQ)AAI10656696
035 $a AAI10656696
040 $a MiAaPQ $b eng $c MiAaPQ
100 1 $a Howard, Brent Ernest. $3 1186198
245 1 0 $a Corrosion of Aluminum Alloys - Polymer Matrix Composite Interfaces in Diverse Natural Atmospheric Environments.
264 0 $c 2017
300 $a 1 online resource (148 pages)
336 $a text $b txt $2 rdacontent
337 $a computer $b c $2 rdamedia
338 $a online resource $b cr $2 rdacarrier
500 $a Source: Masters Abstracts International, Volume: 56-06.
500 $a Adviser: Lloyd H. Hihara.
502 $a Thesis (M.S.)--University of Hawai'i at Manoa, 2017.
504 $a Includes bibliographical references
520 $a The environmental corrosion of carbon-fiber/epoxy and E-glass/epoxy composite laminated aluminum alloys [e.g., Al 1100-H14, Al 5456-H116 (non-sensitized), Al 5456-H116 (sensitized), and Al 7075-T6] was studied to characterize the interfacial corrosion between the composite and the aluminum substrate. Samples were exposed at 5 locations around the islands of Hawai'i that represented alpine, marine, severe marine, rainforest, and volcano environments over 1-month, 6- month, and 12-month time periods. After exposure, the samples were then adhesion strength tested by conducting pull test to remove the composite laminate from the aluminum substrate to determine the loss (if any) of the composite laminate adhesion to their respective aluminum substrates. The delaminated samples were then analyzed with a scanning electron microscope and energy dispersive X-ray analysis to determine the distribution of corrosion products and ionic species at the aluminum substrate - composite laminate interfaces. The decay in adhesion strength was correlated to the amount of corrosion at the interface that was dependent on the type of composite and type of aluminum alloy.
533 $a Electronic reproduction. $b Ann Arbor, Mich. : $c ProQuest, $d 2018
538 $a Mode of access: World Wide Web
650 4 $a Mechanical engineering. $3 557493
650 4 $a Engineering. $3 561152
650 4 $a Naval engineering. $3 1185951
655 7 $a Electronic books. $2 local $3 554714
690 $a 0548
690 $a 0537
690 $a 0468
710 2 $a ProQuest Information and Learning Co. $3 1178819
710 2 $a University of Hawai'i at Manoa. $b Mechanical Engineering. $3 1186199
856 4 0 $u http://pqdd.sinica.edu.tw/twdaoapp/servlet/advanced?query=10656696 $z click for full text (PQDT)